Utilization of natural zeolite in aerated concrete production

Authors :
Cenk Karakurta, Haldun Kuramab, İlker Bekir Topçuc

Abstract :

In this study, natural zeolite (clinoptilolite) was used as an aggregate and bubble-generating agent in autoclaved aerated concrete (AAC) production. The crushed and grinded samples were classified into two different particle sizes: 100 μm (fine-ZF) and 0.5–1 mm (coarse-ZC) before using in AAC mixtures. The effects of particle size, replacement amount (25%, 50%, 75% and 100% against quartz) and curing time on the AAC properties were experimentally investigated. It was found that usage of natural zeolite, especially with a coarser particle size, has beneficial effect on the physical and mechanical properties of AAC. The optimum replacement amount was determined as 50% and at this rate the compressive strength, unit weight and thermal conductivity of AAC were measured as 3.25 MPa, 0.553 kg/dm3 and 0.1913 W/mK, respectively. Scanning electron microscopy analysis also confirmed the above findings. Denser C–S–H structures were obtained up to a replacement amount of 50%. Finally, the test results demonstrated that calcined zeolite acts as both an aggregate and a bubble-generating agent, and that AAC with a compressive strength of 4.6 MPa and unit weight of 0.930 kg/dm3 can be produced without aluminum powder usage.

Keywords :
Autoclaved aerated concrete, Microstructure, Natural zeolite, Thermal conductivity

Source :
http://www.sciencedirect.com/science/article/pii/S0958946509001498